In the future, we will try to use new technology to create new business value and to contribute to research and product development for the Bimetallic Wear Resistant Alloy Pipe, Wear Protection Alumina Ceramic Sheet, Composite Bimetal Hardfacing Plate. We strengthen the alliance, collaboration, reinvestment and joint development overseas. The company pays attention to modern management and keeps developing internationally.
Description
Bimetal hardfacing wear plates, its substrate using common Q235B steel plate, and Wear-resisting layer is composed of advanced alloy welding which was joint research and development by our company and scientific research institutions.
1 bimetal wear steel plate is a kind of the spray welding technology to produce the high wear resistance, resistance to erosion of composite materials
2 Chromium carbide layer with high hardness has good wear-resistant performance, and the substrate have most widely using because of its moderate carbon, good comprehensive performance , strength and welding
3 Bimetal hardfacing wear plates can be easily formed to suit curves and contours. Welded studs or countersunk inserts can be fitted so the plates can easily replaceable.
4 The chromium carbide allow this wear plate to be supported under extreme wear and strong impact including of truck deck liners, hoppers, shutes
5 The substrate is not fixed, the plate can be chose according to customers needing. Different thickness is allowed according to your demand.
Technical details of the Bimetal Wear Hardfacing Steel Plate
| Product Name | HH-700B abrasion composite plate |
| Material | High chromium carbide overlay abrasion resistant steel |
| Thickness | 4+4 5+3 6+4 6+5 8+4 8+6 8+8 10+4 10+6 10+8 10+10 12+4 |
| 12+6 12+8 12+10 14+6 14+8 14+10 16+6 16+8 16+10 16+12 | |
| etc. or as customized | |
| Weldable Thickness | 3-20mm |
| Hardness | HRC 52-62 Wear deposite 3mm: HRC 52-58, 4mm: HRC 56-60,5mm:HRC 57-62，6mm:HRC 57-62,8mm:HRC 58-62,10mm: HRC 60-62,12mm:>HRC 62 HRC of 1 layer:52-58,2 layer: 58-62, Pure weld deposite: 62 |
| Surface Treatment | Hardfacing clading coated. |
| Technique | Advanced automatic self-shilded open arc welding |
| Chemical Composition of the wear deposite | Take 6+6 abrasion composite plate for example: C:4.3-4.8% Cr:23-30% Mn:0.8-1.1% Mo:0.08-0.18 Ni:0.08-0.15,Other Metal elements:Micro |
| Base Plate | Q235B,AIl weldable steels,mostly structural steels. |
| Feature | High wear resistance 12-20 times higher than common plate 5-10 times than low alloy steel plate 2-3 times than high chromium cast iron plate |
Packing details
Why Choose Us?
1. We are the manufacture in bimetal hardfacing wear plate with more than 10 years.
2.Quality is our culture.
3.Different sizes and shapes are customised.
4.Professional technical team and after sales team had.
5.We have rich experience in mining units and cement plants.
6.Free samples are provided for your test.
Our Company
We are a manufacturing enterprise integrating R & D, manufacture and installation. It is an experienced manufacturer specializing in providing wear-resistant technical solutions and supporting wear-resistant products. We develops and manufactures custom solutions for the protection of industrial facilities from wear and impact damage. Our wear-resistant materials and products for industrial plants offer customer-specific solutions which allows us to assure the proper flow of materials and secure your production equipment against unplanned downtime.
Our company now has complete online and offline sales channels, complete and scientific quality management system, and our Chromium Carbide Cco Wear Resistant Plate Wear Plate are sold all over the world. The company realizes the integration of education and industry, relying on the unique resources of universities to find talents from the source. Our company pursues excellence in quality policy.