Our company will continue to be based on the market, focus on the industry, persevere and help the development of Wear Resistant Chromium Carbide Overlay Plate, Wear Resistant Ceramic Liners, Alumina Ceramic Tube With Wear Resistance industry. The company has more than one production equipment and testing instruments. The company operates in good faith and abides by the law, and has been well received by customers and users. Our development direction is: take the technological innovation as the core, take the customer's demand as the guidance.
Description
Bimetal hardfacing wear plates, its substrate using common Q235B steel plate, and Wear-resisting layer is composed of advanced alloy welding which was joint research and development by our company and scientific research institutions.
1 bimetal wear steel plate is a kind of the spray welding technology to produce the high wear resistance, resistance to erosion of composite materials
2 Chromium carbide layer with high hardness has good wear-resistant performance, and the substrate have most widely using because of its moderate carbon, good comprehensive performance , strength and welding
3 Bimetal hardfacing wear plates can be easily formed to suit curves and contours. Welded studs or countersunk inserts can be fitted so the plates can easily replaceable.
4 The chromium carbide allow this wear plate to be supported under extreme wear and strong impact including of truck deck liners, hoppers, shutes
5 The substrate is not fixed, the plate can be chose according to customers needing. Different thickness is allowed according to your demand.
Technical details of the Bimetal Wear Hardfacing Steel Plate
| Product Name | HH-700B abrasion composite plate |
| Material | High chromium carbide overlay abrasion resistant steel |
| Thickness | 4+4 5+3 6+4 6+5 8+4 8+6 8+8 10+4 10+6 10+8 10+10 12+4 |
| 12+6 12+8 12+10 14+6 14+8 14+10 16+6 16+8 16+10 16+12 | |
| etc. or as customized | |
| Weldable Thickness | 3-20mm |
| Hardness | HRC 52-62 Wear deposite 3mm: HRC 52-58, 4mm: HRC 56-60,5mm:HRC 57-62，6mm:HRC 57-62,8mm:HRC 58-62,10mm: HRC 60-62,12mm:>HRC 62 HRC of 1 layer:52-58,2 layer: 58-62, Pure weld deposite: 62 |
| Surface Treatment | Hardfacing clading coated. |
| Technique | Advanced automatic self-shilded open arc welding |
| Chemical Composition of the wear deposite | Take 6+6 abrasion composite plate for example: C:4.3-4.8% Cr:23-30% Mn:0.8-1.1% Mo:0.08-0.18 Ni:0.08-0.15,Other Metal elements:Micro |
| Base Plate | Q235B,AIl weldable steels,mostly structural steels. |
| Feature | High wear resistance 12-20 times higher than common plate 5-10 times than low alloy steel plate 2-3 times than high chromium cast iron plate |
Packing details
Why Choose Us?
1. We are the manufacture in bimetal hardfacing wear plate with more than 10 years.
2.Quality is our culture.
3.Different sizes and shapes are customised.
4.Professional technical team and after sales team had.
5.We have rich experience in mining units and cement plants.
6.Free samples are provided for your test.
Our Company
We are a manufacturing enterprise integrating R & D, manufacture and installation. It is an experienced manufacturer specializing in providing wear-resistant technical solutions and supporting wear-resistant products. We develops and manufactures custom solutions for the protection of industrial facilities from wear and impact damage. Our wear-resistant materials and products for industrial plants offer customer-specific solutions which allows us to assure the proper flow of materials and secure your production equipment against unplanned downtime.
We promise to exchange our best quality Mineral Industrial Use Wear Resistant Composite Bimetal Steel Plates for Industrial ... and considerate service for the success of our cooperation with all customers! No matter how the times develop, we will be meticulous in the pursuit of product quality. The essence of corporate governance is to create a cohesive force to realize the common value of the company and form a corporate culture.